17-4PH Stainless Steel Plate

17-4PH Stainless Steel Plate
Product Description

17-4 PH is a martensitic, chromium-nickel-copper precipitation-hardening stainless steel. 17-4PH Stainless Steel Plate is capable of attaining a wide range of strength and toughness properties depending on the precipitation or aging temperature used in hardening. 17-4PH SS Plate is valuable combination of high strength, good corrosion resistance and toughness in both base metals and welds gives designers opportunities to add reliability to their products while simplifying fabrication and often reducing costs. High strength is maintained to approximately 600°F (316°C). This material has good resistance to stress corrosion cracking in the lower strength conditions.

Standard Inventory Specifications:
  • UNS S17400
  • AMS 5604
  • ASTM A 693
  • ASME SA 693
  • W.NR. 1.4542
  • PWA-LCS
  • GE-S400/S1000
  • RR SABRe Edition 2
  • DFARS Compliant

 

Inventory Size Range:

  • Sheet : 0.029" - 0.130"
  • Plate : 0.1875" - 2.500"

The technical data provided is for information only and not for design purposes. It is not warranted or guaranteed

Element

Percent By Weight Type 17-4ph

C

Carbon

0.07 maximum

Mn

Manganese

1.00 maximum

P

Phosphorus

0.04 maximum

S

Sulfur

0.03 maximum

Si

Silicon

1.00 maximum

Cr

Chromium

15.00 - 17.50

Ni

Nickel

3.00 - 5.00

Cu

Copper

3.00 - 5.00

Nb
Ta

Columbium
plus Tantalum

0.15 - 0.45


Common Applications of 17-4PH Stainless Steel Plate:

  • Aerospace applications
  • Fasteners
  • Base plates
  • Chemical processing equipment
  • Oil and petroleum refining equipment
  • Nuclear components
  • Food grade stainless steel for processing equipment
  • General metalworking applications that call for precipitation-hardening stainless steel

17-4PH Physical Properties:

  • Melting Range: 2560-2625°F (1404-1440°C)
  • Density: 0.2820 lb/in³

Temperature Range

Coefficients

°C

°F

μm/m·°C

in/in/°F·106

21-93

70-200

10.8

6

21-204

70-400

10.8

6

21-316

70-600

11.2

6.2

21-427

70-800

11.2

6.3


Thermal Conductivity (H 900 Condition)

Temperature Range

W/m·K

Btu/(hr/ft²/in/°F)

°C

°F

149

300

17.9

124

260

500

19.5

135

460

860

22.5

156

482

900

22.6

157


Electrical Resistivity (Annealed Condition)

Mean Coefficient of Thermal Expansion (Annealed Condition)

Microhm-cm: 98

Mechanical Properties and Yield Strength 17-4PH Stainless Steel - Cold Flattened (Annealed)

  • Ultimate Tensile Strength Ksi (MPa): 160 (1103)
  • 0.2% Tensile Yield Strength Ksi (MPa): 145 (1000)
  • Elongation % in 2" (50mm): 5.0
  • Hardness Rockwell C: 35